| Properties |
UV Bond – 01 |
UV Flex – 01 |
UV Pot – 01 |
| Chemistry |
Acrylated Urethane |
Acrylated Urethane |
Modified Acrylate |
| Mix Ratio |
One Part |
One Part |
One Part |
| Color |
Transparent liquid |
Bone white to milky translucent |
Transparent liquid |
| Curing Condition |
UV/Vis Light Cure |
UV/Vis Light Cure |
UV/Vis Light Cure |
| Cure Depth , mm |
>3.5 |
>3.5 |
0.25 – 5.00 |
| Complete Curing Energy mJ/cm2 |
>1200 |
>1200 |
|
| Index of Refraction |
|
|
1.48 |
| Viscosity (mPa.s) |
18,000 – 35000 |
18,000 – 35000 |
1200-2000 |
| Tack free Time @25℃ |
5s |
3s |
1-20s |
| Density(g/cc) |
1.12 |
1.12 |
1.03 |
| Hardness |
65D |
60D |
75D |
| Tensile Strength (Mpa) |
23 |
PC-PC: >12
PC-PVC: >9
PC-AL: >7 |
Yield: 38.6
Break: 36.6 |
| Elongation (%) |
265 |
90 |
6 |
| Tensile Modulus (Mpa) |
|
|
1384 |
| Shear Strength (Mpa) |
|
|
Glass-Glass: 8.1 |
| Block Shear Strength (Mpa) |
|
|
Steel-Glass: 8.3
Al-Glass: 4.1
Stainless-Glass: 2.6
G-10 Epoxyglass-Glass: 3.4
PVC-Glass: 2.8
ABS-Glass: 1
PC-Glass: 1.2
Acrylic-Glass: 1 |
| Dielectric Strength (kv/mm) |
28 |
28 |
|
| Dielectric Constant (1MHz) |
4 |
4 |
|
| Dielectric loss (1MHz) |
0.023 |
0.023 |
|
| Volume resistivity (Ω.cm) |
|
8.7 x 1014 |
|
| Storage conditions |
8-28℃, ≤60%RH |
8-28℃, ≤60%RH |
8-28℃, ≤60%RH |
| Shelf life |
12 months |
12 months |
12 months |
| Benefit |
*Designed for bonding rigid and flexible PVC to PC
*Flexibility of the bond improved load bearing capacity and shock absorption
*Adhered to wide variety of substrates: glass, plastic and metals |
*Designed for bonding rigid and flexible PVC to PC
*Suitable for large gap filling (0.25mm) and flexible joint
*Adhered to wide variety of substrates: glass, plastic and metals |
*Fast UV cure for impact resistant bond
*Suitable for bonding, sealing and potting application of glass or other materials
*Self levelling |
| Operating Temperature |
-50℃-150℃ |
-50℃-150℃ |
-55℃-150℃ |
| Others |
30ml/Bottle; 1kg/ Barrel |
30ml/Bottle; 1kg/ Barrel |
50ml/250ml tube, 1kg barrels |